Lateral Ge Diffusion During Oxidation of Si/SiGe Fins

This Letter reports on the unusual diffusion behavior of Ge during oxidation of a multilayer Si/SiGe fin. It is observed that oxidation surprisingly results in the formation of vertically stacked Si nanowires encapsulated in defect free epitaxial strained Si_xGe_1-x. High angle annular dark field scanning transmission electron microscopy (HAADF-STEM) shows that extremely enhanced diffusion of Ge occurs along the vertical Si/SiO₂ oxidizing interface and is responsible for the encapsulation process. Further oxidation fully encapsulates the Si layers in defect free single crystal Si_xGe_1-x (x up to 0.53), which results in Si nanowires with up to -2% strain. Atom probe tomography reconstructions demonstrate that the resultant nanowires run the length of the fin. We found that the oxidation temperature plays a significant role in the formation of the Si nanowires. In the process range of 800-900 °C, pure strained and rounded Si nanowires down to 2 nm in diameter can be fabricated. At lower temperatures, the Ge diffusion along the oxidizing Si/SiO₂ interface is slow, and rounding of the nanowire does not occur, while at higher temperatures, the diffusivity of Ge into Si is sufficient to result in dilution of the pure Si nanowire with Ge. The use of highly selective etchants to remove the SiGe could provide a new pathway for the creation of highly controlled vertically stacked nanowires for gate all around transistors.