Fabrication and characterization of chitosan/OGP coated porous poly(ε-caprolactone) scaffold for bone tissue
Zhixiang Cui1,2,3,4, Luyin Lin1,2, Junhui Si1,2
1a School of Materials Science and Engineering, Fujian University of Technology , Fuzhou , China.
Abstract:
As one of the stimulators on bone formation, osteogenic growth peptide (OGP) improves both proliferation and differentiation of the bone cells in vitro and in vivo. The aim of this work was the preparation of three dimensional porous poly(ε-caprolactone) (PCL) scaffold with high porosity, well interpore connectivity, and then its surface was modified by using chitosan (CS)/OGP coating for application in bone regeneration. In present study, the properties of porous PCL and CS/OGP coated PCL scaffold, including the microstructure, water absorption, porosity, hydrophilicity, mechanical properties, and biocompatibility in vitro were investigated. Results showed that the PCL and CS/OGP-PCL scaffold with an interconnected network structure have a porosity of more than 91.5, 80.8%, respectively. The CS/OGP-PCL scaffold exhibited better hydrophilicity and mechanical properties than that of uncoated PCL scaffold. Moreover, the results of cell culture test showed that CS/OGP coating could stimulate the proliferation and growth of osteoblast cells on CS/OGP-PCL scaffold. These finding suggested that the surface modification could be a effective method on enhancing cell adhesion to synthetic polymer-based scaffolds in tissue engineering application and the developed porous CS/OGP-PCL scaffold should be considered as alternative biomaterials for bone regeneration.