An Ex-vivo Shear and tensile bond strengths of orthodontic molar tubes bonded using different techniques
Elham Abu-Alhaija1, Mohammad Jaradat2, Ahed Alwahadni3
1Professor, Department of Preventive Dentistry, Faculty of Dentistry, Jordan University of Science and Technology, Irbid-Jordan.
Background:
Molar bonding procedures need continuous improvement to be widely accepted clinically and eventually replace molar bands.
Material And Methods:
The purpose of this study was to determine the effects of enamel micro-abrasion and silane coating of the base of molar tubes on shear and tensile bond strengths of orthodontic molar tubes. A total of 200 third molars were randomly allocated into five groups of 40 teeth as follows: group 1: molar tubes bonded to etched teeth (37% phosphoric acid gel; control group); group 2: molar tubes bonded to etched teeth (37% phosphoric acid) with the addition of silane to the base of molar tubes; group 3: molar tubes bonded to teeth pre-treated with 18% hydrochloric acid and pumice (micro-abrasion); group 4: molar tubes bonded to teeth pre-treated with microabrasion with the addition of silane to the base of molar tubes; group 5: molar tubes bonded to teeth pre-treated with microabrasion before conventional acid etching combined with the addition of silane to the base of molar tubes. The bond strength testing was performed using a computer control electromechanical universal testing machine.
Results:
The highest mean shear and tensile bond strengths were recorded in group 5 (13.81±2.54MPa and 13.97±2.29 MPa, respectively). Micro-abrasion alone (group 3) and the combination of enamel micro-abrasion and the addition of silane (group 4) produced bond strength values comparable to the control.
Conclusions:
Enamel surface pre-treatment (micro abrasion) before conventional acid etching combined with the addition of silane to the base of the molar tube produced the highest bond strengths among all tested groups. Key words:Molar, shear strength, tensile strength, orthodontic appliances.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
08:46Force System with Vertical V-Bends: A 3D In Vitro Assessment of Elastic and Rigid Rectangular Archwires
Published on: July 24, 2018
Related Concept Videos
01:12Bonding and Strength of Aggregate
01:15Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity
01:23Stresses under Combined Loadings
The process begins by slicing the tube at critical points and analyzing the internal forces and stress components at these sections, focusing on the centroid. Normal stresses, generated by axial forces and bending moments, are either compressive or tensile and vary across the section from...