Facile Preparation of Titanium(IV)-Immobilized Hierarchically Porous Hybrid Monoliths

Hierarchically porous materials have become a key feature of biological materials and have been widely applied for adsorption or catalysis. Herein, we presented a new approach to directly prepare a phosphate-functionalized hierarchically porous hybrid monolith (HPHM), which simultaneously contained mesopores and macropores. The design was based on the copolymerization of polyhedral oligomeric vinylsilsesquioxanes (vinylPOSS) and vinylphosphonic acid (VPA) by adding degradable polycaprolactone (PCL) additive. The phosphate groups could be directly introduced into the hybrid monoliths. This approach was simple and time-saving, and overcame the defect of a rigorous, complex process for preparing traditional Ti⁴⁺-immobilized metal ion affinity chromatography (IMAC) materials. The specific surface area of an optimal hybrid monolith could reach 502 m²/g obtained by nitrogen adsorption/desorption measurements, which originated from the degradation of PCL. Meanwhile, the characterization of scanning electron microscopy (SEM) and mercury intrusion porosimetry (MIP) also suggested that the macropores existed in the hybrid monoliths. The size of macropores could be controlled by the content of PCL in the polymerization mixture. The prepared Ti⁴⁺-IMAC HPHMs exhibited high adsorption capacity (63.6 mg/g for pyridocal 5'-phosphatemonohydrate), and excellent enrichment specificity (tryptic digest of β-casein/BSA at a molar ratio of 1:1000) and sensitivity (tryptic digest of 5 fmol of β-casein). Moreover, the Ti⁴⁺-IMAC HPHMs provided effective enrichment ability of low-abundance phosphopeptides from human serum and HeLa cell digests.