Preparation and Characterization of Zirconia-Coated Nanodiamonds as a Pt Catalyst Support for Methanol
Jing Lu1, Jianbing Zang2,3, Yanhui Wang4,5
1Institute of Manufacturing Engineering, Huaqiao University, Xiamen 361021, China. lujing26@hqu.edu.cn.
Abstract:
Zirconia-coated nanodiamond (ZrO₂/ND) electrode material was successfully prepared by one-step isothermal hydrolyzing from ND-dispersed ZrOCl₂·8H₂O aqueous solution. High-resolution transmission electron microscopy reveals that a highly conformal and uniform ZrO₂ shell was deposited on NDs by this simple method. The coating obtained at 90 °C without further calcination was mainly composed of monoclinic nanocrystalline ZrO₂ rather than common amorphous Zr(OH)₄ clusters. The ZrO₂/NDs and pristine ND powder were decorated with platinum (Pt) nanoparticles by electrodeposition from 5 mM chloroplatinic acid solution. The electrochemical studies indicate that Pt/ZrO₂/ND catalysts have higher electrocatalytic activity and better stability for methanol oxidation than Pt/ND catalysts in acid.
More Related Videos
08:13Chemical Precipitation Method for the Synthesis of Nb2O5 Modified Bulk Nickel Catalysts with High Specific Surface Area
Published on: February 19, 2018
08:40Synthesis of Metal Nanoparticles Supported on Carbon Nanotube with Doped Co and N Atoms and its Catalytic Applications in Hydrogen Production
Published on: December 6, 2021