Ultrafast Formation of Amorphous Bimetallic Hydroxide Films on 3D Conductive Sulfide Nanoarrays for
Xu Zou1, Yipu Liu1, Guo-Dong Li1
1State Key Laboratory of Inorganic Synthesis and Preparative Chemistry, College of Chemistry, Jilin University, Changchun, 130012, P. R. China.
Abstract:
Developing nonprecious oxygen evolution electrocatalysts that can work well at large current densities is of primary importance in a viable water-splitting technology. Herein, a facile ultrafast (5 s) synthetic approach is reported that produces a novel, efficient, non-noble metal oxygen-evolution nano-electrocatalyst that is composed of amorphous Ni-Fe bimetallic hydroxide film-coated, nickel foam (NF)-supported, Ni3 S2 nanosheet arrays. The composite nanomaterial (denoted as Ni-Fe-OH@Ni3 S2 /NF) shows highly efficient electrocatalytic activity toward oxygen evolution reaction (OER) at large current densities, even in the order of 1000 mA cm-2 . Ni-Fe-OH@Ni3 S2 /NF also gives an excellent catalytic stability toward OER both in 1 m KOH solution and in 30 wt% KOH solution. Further experimental results indicate that the effective integration of high catalytic reactivity, high structural stability, and high electronic conductivity into a single material system makes Ni-Fe-OH@Ni3 S2 /NF a remarkable catalytic ability for OER at large current densities.