Synthesis and characterization of Bioglass-based bone grafts with Gelatine substitution for biomedical applications
1Dept Metallurgy and Mater Eng, Faculty of Chemical and Metallurgy, Yildiz Technical University, Istanbul, Turkey.
Background:
Syntesizing alternative bone graft materials are important in biomedical applications. Their morphology, mechanical properties and cell viability plays an important role in tissue engineering.
Objective:
Bioglass (B) based bone grafts with Gelatin (G) substitution were syntesized via the sol-gel method and were compared with various Gelatin and Bioglass concentrations (wt%).
Methods:
Syntesized bone grafts were characterized by Scanning Electron Microscopy (SEM) and X-ray diffraction (XRD) to show the structural and morphological changes of the fabricated B-based bone grafts.
Results:
It was demonstrated that the concentration of pore size increased with increasing amounts of Gelatin in wt%. The biograft-B40G20 produced the highest flexture strength and hardness. Increasing the pore size caused a decrease in hardness and flexture stress of B-based biografts.
Conclusions:
Cell viability tests were conducted on the fabricated biografts and it was shown that the cell viability increased in fabricated B-based bone grafts.