Comparative Evaluation of Bond Strength and Microleakage of Standard and Expired Composite at Resin-Dentin Interface:
Nidhi Talreja1, Shilpy Singla2, N D Shashikiran3
1Postgraduate Student, Department of Pedodontics and Preventive Dentistry, People's College of Dental Sciences and Research Centre, People's University, Bhopal, Madhya Pradesh, India.
Background:
Evaluation of bond strength and microleakage caused by polymerization shrinkage provides a screening mechanism and an indication of the potential for the clinical success of composite restorations.
Aim:
The aim of this study was to determine the effect on shear bond strength and microleakage of standard and expired composites.
Materials And Methods:
Selected specimens were etched using 37% phosphoric acid for 15 seconds and were randomly divided into four groups. Group I: Standard composite and bonding agent; group II: Expired composite and bonding agents; group III: Standard composite and expired bonding agent; and group IV: Expired composite and standard bonding agent. Specimens were further subdivided into two subgroups. In subgroup A, specimens were sheared with a universal testing machine, and the results were calculated in MPa; in subgroup B, specimens was sectioned longitudinally and analyzed for leakage (dye penetration) using a stereomicroscope.
Results:
The results of the present study showed that acceptable values for bond strength and microleakage were obtained even if one of the components of the dental resin composite is expired.
Conclusion:
In Indian scenario, the expired composite material may provide some assistance in compromised clinical situations. It can be used as an interim restoration and compensate for the high material cost.
How To Cite This Article:
Talreja N, Singla S, Shashikiran ND. Comparative Evaluation of Bond Strength and Microleakage of Standard and Expired Composite at Resin-Dentin Interface: An in vitro Study. Int J Clin Pediatr Dent 2017;10(1):1-4.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
04:23Standardized Protocol to Evaluate the Effect of Surface Treatments, Luting Cements, and Thermocycling on PEEK–Composite Bond Strength
Published on: June 9, 2026