Cell viability and hemocompatibility evaluation of a starch-based hydrogel loaded with hydroxyapatite or calcium
Juan Carlos Flores-Arriaga1, Amaury de Jesús Pozos-Guillén1, Diana María Escobar-García1
1Universidad Autónoma de San Luis Potosí, San Luis Potosí, México.
Abstract:
The objective of this study is to evaluate the cell viability and hemocompatibility of starch-based hydrogels for maxillofacial bone regeneration. Seven starch-based hydrogels were prepared: three loaded with 0.5, 1 and 2% calcium carbonate (Sigma Aldrich, St. Louis, MO, USA); three loaded with 2, 3 and 4% hydroxyapatite (Sigma Aldrich); and one not loaded as a control. A 10 M NaOH was then added to induce hydrogel formation. Human osteoblasts were cultured on each hydrogel for 72 h. An MTS assay (Cell Titer96; PROMEGA, Madison, WI, USA) was used to assess cell viability. Hemocompatibility testing was conducted with normal human blood in the following conditions: 100 mg of each hydrogel in contact with 900 µL of whole blood for 15 min at 37 °C under lateral stirring. Higher percentages of cell viability were observed in starch-based hydrogels loaded with hydroxyapatite as compared with the control. The hemolysis test showed a hemolysis level lower than 2%. Activated partial thromboplastin time and prothrombin time were unchanged, while platelet counting showed a slight decrease when compared with controls.