Enhanced mechanical properties and biocompatibility of novel hydroxyapatite/TOPAS hybrid composite for bone tissue...

The bioactivity and mechanical properties of hybrid composites of hydroxyapatite (HA) in cyclic olefinic copolymer (COC) also known commercially as TOPAS are investigated, first time, for regeneration and repair of the bone tissues. HA is synthesized to obtain the spherically shaped nanoparticles in the size range of 60±20nm. Various concentrations of HA ranging from 1 to 30wt% are dispersed in TOPAS using sodium dodecyl sulfate (SDS) coupling agent for better dispersion and interaction of hydrophilic HA with hydrophobic TOPAS. Scanning electron microscope shows the uniform dispersion of HA≤10wt% in TOPAS and at higher concentrations >10wt%, agglomeration occurs in the hybrid composites. Tunable mechanical properties are achieved as the compressive modulus and strength are increased around 140% from 6.4 to 15.3MPa and 185% from 0.26 to 0.74MPa, respectively. Such increase in the mechanical properties of TOPAS is attributed to the anchoring of the polymer chains in the vicinity of HA nanoparticles owing to better dispersion and interfacial interactions. In comparison to neat TOPAS, hybrid composites of TOPAS/HA promoted the cell adhesion and proliferation significantly. The cell density and proliferation of TOPAS/HA hybrid composites is enhanced 9 and 3 folds, respectively, after 1day culturing in preosteoblasts cells. Moreover, the morphology of cells changed from spherical to flattened spread morphology demonstrating clearly the migration of the cells for the formation of interconnected cellular network. Additionally, very few dead cells are found in hybrid composites showing their cytocompatibility. Overall, the hybrid composites of TOPAS/HA exhibited superior strength and stiffness along with enhanced cytocompatibility for bone tissue engineering applications.