A high performance and highly-controllable core-shell imprinted sensor based on the surface-enhanced Raman scattering...

A novel, sensitive sensor material combined the technique of surface enhance Raman scattering (SERS) and molecular imprinting was prepared. It was used the amino-functionalized SiO₂ nanospheres as the supporting materials and anchored Ag nanoparticles on the surface by the function of coordination between Ag⁺ and NH₂^-. Then, it was used that the Rhodamine 6G (R6G) as the template, acrylamide (AM) as functional monomer, ethyleneglycol dimethacrylate (EGDMA) as cross-linker, 2,2'-azobis(2-methylpropionitrile) (AIBN) as initiator to prepare the core-shell molecular imprinted polymers. Prominently, the shell thickness could be controlled by the regulation of cross-linker dosage and it was found that the SERS detection signal was most obvious when the shell thickness was about 40nm. Under the optimal condition, it was presented good linear relationship (R²=0.93) between the Raman signal (at 1505cm^-1) and the concentration of the templates and the limit of detection was 10^-12molL^-1. Meanwhile, the selective experiment was proved that this materials owned specific selectivity to the template. It was confirmed that the core-shell molecular imprinted polymers were a kind of highly sensitive and selective sensor materials in the field of R6G detection.