Solution Blow Spinning of Food-Grade Gelatin Nanofibers

The primary advantage of nanofibers over larger diameter fibers is the larger surface area to volume ratio. This study evaluated solution blow spinning (SBS) processing conditions for obtaining food-grade gelatin nanofibers from mammalian and fishery byproducts, such as pork skin gelatins (PGs) and high molecular weight fish skin gelatin (HMWFG). HMWFG had a highest intact collagen structure compared to PGs. PGs with different Bloom values, solution viscosities, and surface tensions were compared with HMWFG for their ability to produce nanofibers through SBS. Only HMWFG fibers were obtained irrespective of processing conditions, which looked like fluffy cotton candy. HMWFG nanofibers had round morphologies with a narrower diameter distribution and lower average fiber diameter (AFD) under medium gelatin concentrations, medium air pressures, and medium feed rates. The highest glass transition temperature (T_g ) values were obtained at medium concentrations, medium air pressure, and either high or low feed rate. The thinnest HMWFG nanofibers with an AFD of 80.1 nm and the highest T_g value of 59.0 °C could be formed by combining a concentration of 17.6% (w/v), an air pressure of 0.379 MPa, and a feed rate of 0.06 mL/min from the response surface analysis. HMWFG Brunauer, Emmett, and Teller surface area increased from 221 to 237 m² /g, indicating their potential applicability for active compound carrier.