A facile route towards PDMAEMA homopolymer amphiphiles

Well-defined poly(2-(dimethylamino)ethyl methacrylate) (PDMAEMA) has been modified at low degrees of quaternization of the tertiary amine groups using alkyl halides with long alkyl chains as the quaternization agents. The resulting PDMAEMA-co-PQDMAEMA copolymers were studied in aqueous solution using potentiometric titrations, turbidimetry, surface tensiometry, dynamic light scattering and zeta potential measurements. An increase of the hydrophilicity of the precursor polymer, leading to an increase or even elimination of the lower critical solution temperature (LCST) for the quaternized copolymers was found; this extended the temperature range of the stable polymer solution. At the same time, it was shown that the hydrophobic character of the polymer increases upon quaternization, leading to higher surface activity compared to the precursor PDMAEMA homopolymer, and, thus, to more effective polymeric surfactants. This contradiction in the copolymer behavior was attributed to the interplay between the polymer self-assembly in the aqueous medium and the polymer adsorption at the air/water interface, which dominate the cloud point and the surface properties, respectively.