Preparation and characterization of small-diameter decellularized scaffolds for vascular tissue engineering in an...

The development of a suitable extracellular matrix (ECM) scaffold is the first step in vascular tissue engineering (VTE). Synthetic vascular grafts are available as an alternative to autologous vessels in large-diameter arteries (>8 mm) and medium-diameter arteries (6-8 mm). In small-diameter vessels (<6 mm), synthetic vascular grafts are of limited use due to poor patency rates. Compared with a vascular prosthesis, natural tissue ECM has valuable advantages. Despite considerable progress in recent years, identifying an optimal protocol to create a scaffold for use in small-diameter (<6 mm) fully natural tissue-engineered vascular grafts (TEVG), remains elusive. Although reports on different decellularization techniques have been numerous, combination of and comparison between these methods are scarce; therefore, we have compared five different decellularization protocols for making small-diameter (<6 mm) ECM scaffolds and evaluated their characteristics relative to those of fresh vascular controls.

The protocols differed in the choice of enzymatic digestion solvent, the use of non-ionic detergent, the durations of the individual steps, and UV crosslinking. Due to their small diameter and ready availability, rabbit arteria carotis were used as the source of the ECM scaffolds. The scaffolds were subcutaneously implanted in rats and the results were evaluated using various microscopy and immunostaining techniques.

Our findings showed that a 2 h digestion time with 1× EDTA, replacing non-ionic detergent with double-distilled water for rinsing and the application of UV crosslinking gave rise to an ECM scaffold with the highest biocompatibility, lowest cytotoxicity and best mechanical properties for use in vivo or in situ pre-clinical research in VTE in comparison.