Potential biodegradable Zn-Cu binary alloys developed for cardiovascular implant applications

Binary Zn-Cu alloy system is developed as potential biodegradable materials for cardiovascular implant application. The microstructure, tensile properties, in vitro corrosion behavior, cytotoxicity and antibacterial property of as-extruded Zn-xCu (x=1, 2, 3, and 4wt%) alloys are investigated systematically. It shows that as Cu content increases more CuZn₅ phase precipitates. After extrusion, the CuZn₅ phases are broken and the grains of Zn-xCu alloys are refined. Tensile test shows that Cu addition could significantly improve the mechanical properties of Zn-xCu alloys. Particularly, the elongation of the Zn-4Cu reaches 50.6±2.8%, which could facilitate the micro-tubes processing for stent fabrication. The micro-tubes of 3mm in outer diameter and 0.2mm in thickness as well as vascular stents have been fabricated successfully using the Zn-Cu binary alloy. The degradation rates of Zn-xCu alloys in c-SBF solution are quite low, which vary from 22.1±4.7 to 33.0±1.0μmyear^-1. With increasing Cu concentration, the corrosion rates of the Zn-xCu alloys generally exhibit a little increase compared with pure Zn, which show no significant difference among Zn-xCu alloys. In vitro test shows that Zn-xCu alloys exhibit acceptable cytotoxicity to human endothelial cells and the antibacterial property (S. aureus) is perfect when Cu concentration is higher than 2wt%. Therefore, the newly developed Zn-xCu binary alloys could be promising candidates for biodegradable cardiovascular implant application due to their excellent combination of strength and ductility, low degradation rates, acceptable cytotoxicity and good antibacterial property.