SU-E-I-76: Optimizing Imaging Parameters for a Novel Radiographic Imaging System for the Detection of Corrosion in...

A laboratory-based phase-contrast radiography/tomosynthesis imaging system previously (Med. Phys. Vol. 38, 2353 May 2011) for improved detection of low-contrast soft-tissue masses was used to evaluate the sensitivity for detecting the presence of thin layers of corrosion on aluminum aircraft structures.

The evaluation utilized a test object of aluminum (2.5 inch × 2.5 inch × 1/8 inch) on which different geometric patterns of 0.0038 inch thick anodized aluminum oxide was deposited. A circular area of radius 1 inch centered on the phantom's midpoint was milled to an approximate thickness of 0.022 inches. The x-ray source used for this investigation was a dual focal spot, tungsten anode x-ray tube. The focal used during the investigation has a nominal size of 0.010 mm. The active area of the imager is 17.1 cm × 23.9 cm (2016 × 2816 pixels) with a pixel pitch of 0.085 mm. X-ray tube voltages ranged from 20-40 kVp and source- to-object and object-to-image distances were varied from 20-100 cm. Performance of the phase-contrast mode was compared to conventional absorption-based radiography using contrast ratio and contrast-to-noise ratios (C/N). Phase-contrast performance was based on edge-enhancement index (EEI) and the edge-enhancement-to-noise (EE/N) ratio.

for absorption-based radiography, the best C/N ratio was observed at the lowest kVp value (20 kVp). The optimum sampling angle for tomosynthesis was +/- 8 degrees.

Comparing C/N to EE/N demonstrated the phase-contrast techniques improve the conspicuity of the oxide layer edges. This work provides the optimal parameters that a radiographic imaging system would need to differentiate the two different compounds of aluminum. Subcontractee from Positron Systems Inc. (Boise, Idaho) through United States Air Force grant (AF083-225).