Characterization of Electrode Materials for Lithium Ion and Sodium Ion Batteries Using Synchrotron Radiation Techniques
Published on: November 11, 2013
Visualization of structural evolution and phase distribution of a lithium vanadium oxide (Li1.1V3O8) electrode via an
Qing Zhang1, Andrea M Bruck, David C Bock
1Department of Materials Science and Engineering, Stony Brook University, Stony Brook, NY 11794, USA. kenneth.takeuchi.1@stonybrook.edu esther.takeuchi@stonybrook.edu amy.marschilok@stonybrook.edu.
Abstract:
Li1+nV3O8 (n = 0-0.2) has been extensively investigated as a cathode material for Li ion batteries because of its superior electrochemical properties including high specific energy and good rate capability. In this paper, a synchrotron based energy dispersive X-ray diffraction (EDXRD) technique was employed to profile the phase transitions and the spatial phase distribution of a Li1.1V3O8 electrode during electrochemical (de)lithiation in situ and operando. As annealing temperature during the preparation of the Li1.1V3O8 material has a strong influence on the morphology and crystallinity, and consequently influences the electrochemical outcomes of the material, Li1.1V3O8 materials prepared at two different temperatures, 500 and 300 °C (LVO500 and LVO300), were employed in this study. The EDXRD spectra of LVO500 and LVO300 cells pre-discharged at C/18, C/40 and C/150 were recorded in situ, and phase localization and relative intensity of the peaks were compared. For cells discharged at the C/18 rate, although α and β phases were distributed uniformly within the LVO500 electrode, they were localized on two sides of the LVO300 electrode. Discharging rates of C/40 and C/150 led to homogeneous β phase formation in both LVO500 and LVO300 electrodes. Furthermore, the phase distribution as a function of position and (de)lithiation extent was mapped operando as the LVO500 cell was (de)lithiated. The operando data indicate that (1) the lithiation reaction initiated from the side of the electrode facing the Li anode and proceeded towards the side facing the steel can, (2) during discharge the phase transformation from a Li-poor to a Li-rich α phase and the formation of a β phase can proceed simultaneously in the electrode after the first formation of a β phase, and (3) the structural evolution occurring during charging is not the reverse of that during discharge and takes place homogenously throughout the electrode.