Synthesis of Zeolites Using the ADOR Assembly-Disassembly-Organization-Reassembly Route
Published on: April 3, 2016
Synthesis of a Single-Crystalline Macroporous Layered Silicate from a Macroporous UTL-Type Zeolite and Its
Yusuke Asakura1,2, Naoki Kawaura1, Yoshiyuki Kuroda3,4
1Department of Applied Chemistry, Faculty of Science and Engineering, Waseda University, 3-4-1 Ohkubo, Shinjuku-ku, Tokyo, 169-8555, Japan.
Abstract:
A single-crystalline macroporous layered silicate was obtained for the first time. Firstly, UTL-type zeolite with macropores was prepared hydrothermally under the presence of acetylene black as a macropore template and the subsequent calcination to remove the template. Double four-membered ring (d4r) units in the UTL framework were selectively dissolved to yield a layered silicate with macropores. Intercalation of tetrabutylammonium ions into the macroporous layered silicate is accelerated if compared with that into the same silicate without macropores, indicating the effectiveness of macropores due to easy diffusion. The layered silicate with macropores was converted into PCR-type zeolite with macropores, a hierarchically micro- and macroporous material, through interlayer condensation.