Efficient and Stable Ternary Organic Solar Cells Based on Two Planar Nonfullerene Acceptors with Tunable...

Planar perylene diimides (PDIs), when used as nonfullerene acceptors for organic photovoltaics, are constrained by their large π-aggregation in solid state. To tackle this issue, another planar nonfullerene acceptor 3,9-bis(2-methylene-(3-(1,1-dicyanomethylene)-indanone)-5,5,11,11-tetrakis(4-hexylphenyl)-dithieno[2,3-d:2',3'-d']-s-indaceno[1,2-b:5,6-b']dithiophene (ITIC) with weak crystallinity and near-infrared light absorption is introduced into the PTB7-Th:PDI binary blend to fabricate efficient and stable ternary solar cells. We have finely tuned the PDI/ITIC weight ratio to investigate the influences of individual ITIC and PDI on the optical, electronic, and morphological properties of the PTB7-Th:ITIC:PDI ternary blend. Compared to the binary blend, complementary optical absorption is achieved in all ternary blends. More importantly, it is found that ITIC plays a critical role on largely suppressing the PDI aggregates in the PTB7-Th:PDI blend, while PDI aids to form an interpenetrating network morphology to facilitate charge transport in the PTB7-Th:ITIC blend. Consequently, when the PDI/ITIC ratio is 3:7 (w/w), the PTB7-Th:ITIC:PDI based inverted solar cells exhibit the highest power conversion efficiency of 8.64% due to their favorable out-of-plane π-π stacking, finest phase-separation morphology, and highest charge mobility. Remarkably, the optimal cells that are solution-processed in air show the promising efficiency of 7.09%, suggesting good ambient stability of such ternary solar cells.