Mechanism and optimization for plasma electrolytic liquefaction of sawdust

In this work, plasma electrolytic technology was successfully employed to achieve fast liquefaction of sawdust when polyethylene glycol 200 (PEG 200) and glycerol were used as liquefacient in the presence of the catalyst sulfuric acid. Results showed that H ions could heat the solution effectively during the plasma electrolytic liquefaction (PEL) process. The influence of some key parameters including liquefaction time, catalyst percentage, liquefacient/sawdust mass ratio, and PEG 200/glycerol molar ratio on the liquefaction yield were investigated. Based on the results of single factor experiments, response surface methodology (RSM) was applied to optimize the liquefaction process. Under the optimal conditions that is liquefaction time of 5.10min, catalyst percentage of 1.05%, liquefacient/sawdust mass ratio of 7.12/1 and PEG 200/glycerol molar ratio of 1.40/1, the liquefaction yield reached 99.48%. Hence, it could be concluded that PEL has good application potential for biomass fast liquefaction.