Influence of Various Soluble Carbonates on the Hydration of Portland Cement studied by X-ray Diffraction

Simona Medvešček, Venčeslav Kaučič, Anton Meden

    Acta Chimica Slovenica
    |June 17, 2017
    PubMed

    More Related Videos

    Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent11:14

    Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent

    Published on: February 21, 2017

    12.9K
    Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way07:42

    Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way

    Published on: November 21, 2017

    10.1K

    Related Concept Videos

    Hydration of Cement01:24

    Hydration of Cement

    Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
    1.1K
    Strength and Heat of Hydration01:29

    Strength and Heat of Hydration

    The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
    The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
    777
    Carbonation Shrinkage01:24

    Carbonation Shrinkage

    Atmospheric CO2 penetrates the concrete's pores and, in the presence of moisture, forms carbonic acid, which then reacts with calcium hydroxide in the hydrated cement, forming calcium carbonate. This process reduces the concrete's volume and is termed carbonation shrinkage.
    The concrete's permeability is slightly reduced as calcium carbonate produced during the reaction fills its pores. Furthermore, its strength is slightly enhanced as the water released during the reaction...
    519
    Porosity in Cement Paste01:18

    Porosity in Cement Paste

    The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
    The balance of water to cement in the mix is...
    509
    Pore Size Distribution01:23

    Pore Size Distribution

    In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
    Adequate...
    527
    Types of Cement II01:22

    Types of Cement II

    Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate...
    493