Optimized composition of nanocomposite scaffolds formed from silk fibroin and nano-TiO₂ for bone tissue engineering

Natural silk fibroin (SF) polymer has biomedical and mechanical properties as a biomaterial for bone tissue engineering scaffolds. Freeze-dried porous nanocomposite scaffolds were prepared from silk fibroin and titanium dioxide (TiO₂) nanoparticles as a bioactive reinforcing agent by a phase separation method. In order to fabricate SF/TiO₂ scaffolds, 5, 10, 15 and 20wt% of the TiO₂ were added to the SF. The phase structure, functional groups and morphology of the scaffolds were evaluated using X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy techniques, respectively. Porosity of the scaffolds was measured by Archimedes' Principle. In addition, mechanical properties of prepared scaffolds were evaluated by measuring the compressive strength and compressive modulus. The bioactivity property of these scaffolds was examined for 7, 14, 21 and 28days immersion in simulated body fluid (SBF) at 37°C and the in vitro degradation was studied by incubation in phosphate buffered saline (PBS) at 37°C and pH7.4 for up to 30days. Moreover, the scaffolds' biocompatibility was evaluated by seeding and culture of SaOS-2 osteoblast-like cells and assessment of their proliferation with MTT [3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide] assay. Results showed that the prepared scaffolds had directional porosity and the reduction of porosity in composite scaffolds with higher contents of TiO₂ nanoparticles resulted to an improvement of the mechanical strength. The macroporous structures with open interconnected and directional pores were successfully obtained without applying any porogen or inorganic solvent. The bioactivity of these scaffolds was confirmed by scanning electron microscopy (SEM) showing surface crystallization of the apatite layer proportional to the duration of immersion in the SBF and the degradation rate of scaffolds were increased by increasing the TiO₂ content. The osteoblast-like cells showed a high attachment and proliferation on these scaffolds and their viability was increased with increasing the SF content. Finally, an optimum composition of SF/TiO₂ nanocomposite scaffolds was selected.