Ionic Conductivity and Potential Application for Fuel Cell of a Modified Imine-Based Covalent Organic Framework

We present the novel potential application of imine-based covalent organic frameworks (COFs), formed by the direct Schiff reaction between 1,3,5-tris(4-aminophenyl)benzene and 1,3,5-benzenetricarbaldehyde building blocks in m-cresol or acetic acid, named RT-COF-1 or RT-COF-1Ac/RT-COF-1AcB. The post-synthetic treatment of RT-COF-1 with LiCl leads to the formation of LiCl@RT-COF-1. The ionic conductivity of this series of polyimine COFs has been characterized at variable temperature and humidity, using electrochemical impedance spectroscopy. LiCl@RT-COF-1 exhibits a conductivity value of 6.45 × 10^-3 S cm^-1 (at 313 K and 100% relative humidity) which is among the highest values so far reported in proton conduction for COFs. The mechanism of conduction has been determined using ¹H and ⁷Li solid-state nuclear magnetic resonance spectroscopy. Interestingly, these materials, in the presence of controlled amounts of acetic acid and under pressure, show a remarkable processability that gives rise to quasi-transparent and flexible films showing in-plane structural order as confirmed by X-ray crystallography. Finally, we prove that these films are useful for the construction of proton exchange membrane fuel cells (PEMFC) reaching values up to 12.95 mW cm^-2 and 53.1 mA cm^-2 for maximum power and current density at 323 K, respectively.