Monovalent Cation Doping of CH3NH3PbI3 for Efficient Perovskite Solar Cells
Published on: March 19, 2017
Overcoming the Intrinsic Difference between Hydrophilic CH₃NH₃PbI₃ and Hydrophobic C60 Thin Films to Improve the
Lung-Chien Chen1, Yu-Shiang Lin2, Zong-Liang Tseng3
1Department of Electro-Optical Engineering, National Taipei University of Technology, Taipei 10608, Taiwan. ocean@ntut.edu.tw.
Abstract:
Dimethylformamide/dimethyl sulfoxide solvent mixtures were used as the CH₃NH₃PbI₃ (MAPbI₃) precursor solvent in a one-step spin coating method to fabricate smooth and hydrophilic crystalline MAPbI₃ thin films on top of hydrophobic carbon-60 (C60) thin film for highly efficient photovoltaics. The structural, optical, and excitonic characteristics of the resultant MAPbI₃ thin films were analyzed using X-ray diffraction (XRD), atomic-force microscopy, absorbance spectroscopy, photoluminescence (PL) spectrometry, and nanosecond time-resolved PL. There was a trade-off between the crystallinity and surface roughness of the MAPbI₃ thin films, which strongly influenced the device performance of MAPbI₃-based photovoltaics. The high power conversion efficiency (PCE) of 17.55% was achieved by improving the wettability of MAPbI₃ precursor solutions on top of the C60 thin films. In addition, it was predicted that the fill factor and PCE could be further improved by increasing the crystallinity of the MAPbI₃ thin film while keeping it smooth.