Oxygen deficient α-Fe₂O₃ photoelectrodes: a balance between enhanced electrical properties and trap-mediated losses

Intrinsic doping of hematite through the inclusion of oxygen vacancies (V_O) is being increasingly explored as a simple, low temperature route to preparing active water splitting α-Fe₂O_3- photoelectrodes. Whilst it is widely accepted that the introduction of V_O leads to improved conductivities, little else is verified regarding the actual mechanism of enhancement. Here we employ transient absorption (TA) spectroscopy to build a comprehensive kinetic model for water oxidation on α-Fe₂O_3- . In contrast to previous suggestions, the primary effect of introducing V_O is to block very slow (ms) surface hole - bulk electron recombination pathways. In light of our mechanistic research we are also able to identify and address a cause of the high photocurrent onset potential, a common issue with this class of electrodes. Atomic layer deposition (ALD) of Al₂O₃ is found to be particularly effective with α-Fe₂O_3- , leading to the photocurrent onset potential shifting by ca. 200 mV. Significantly TA measurements on these ALD passivated electrodes also provide important insights into the role of passivating layers, that are relevant to the wider development of α-Fe₂O₃ photoelectrodes.