Histological and micro Computed Tomography analysis of a femoral stress fracture associated with prolonged bisphosphonate use
Related Experiment Video
Updated: Feb 26, 2026
Imaging of the Microstructural Failure Mechanism in the Human Hip
Published on: September 29, 2023
Matthijs Paul Somford1, Leo J van Ruijven2, Peter Kloen3
1Department of Orthopaedic Surgery, Martini Hospital, Groningen, The Netherlands.
Background:
The origin of atypical femoral fractures (AFF) associated with bisphosphonate therapy remains to be elucidated. In this study, a biopsy of an AFF site is analyzed to determine whether microdamage and/or morphological changes are present in the area of the AFF.
Material And Methods:
Cortical bone from an AFF region was obtained during a preventive stabilization in a patient with a symptomatic AFF. This bone was scanned using microCT (resolution=0.01 mm), stained with basic fuchsin and analyzed histologically.
Results:
The diameter of the Haversian canals was higher in the vicinity of the AFF compared to the bone further away from the AFF. The bone mineral density within the cortex ranged from 1020 to 1080 mg HA/cm3. We observed penetration of basic fuchsin into the matrix, which is a tell-tale sign of diffuse damage.
Discussion:
The higher diameter of haversian canals is likely to result in higher local stresses and consequently increased microdamage. The diffuse microdamage in the biopsy may furthermore be directly related to bisphosphonate use, preventing repair of microdamage, and consequently the development of the AFF.
Conclusion:
Increased porosity of the cortex and accumulation of microdamage might have lead to a stress fracture and ultimately a complete AFF.