Effect of Austenitising Temperature on Mechanical Properties of Nanostructured Bainitic Steel

Related Experiment Video

Updated: Feb 25, 2026

Processing of Bulk Nanocrystalline Metals at the US Army Research Laboratory
08:58

Processing of Bulk Nanocrystalline Metals at the US Army Research Laboratory

Published on: March 7, 2018

9.8K

Jing Zhao1, Jiemin Li2, Honghong Ji3

  • 1State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, China. zjjysu@163.com.

Materials (Basel, Switzerland)
|August 5, 2017
PubMed

Keywords:
mechanical propertynanostructured bainitephase transformationsteelmechanical propertiesbainitic steelaustenitisationmicrostructure

More Related Videos

A Novel Biaxial Testing Apparatus for the Determination of Forming Limit under Hot Stamping Conditions07:40

A Novel Biaxial Testing Apparatus for the Determination of Forming Limit under Hot Stamping Conditions

Published on: April 4, 2017

8.0K
An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature14:51

An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature

Published on: September 23, 2018

7.5K

Related Concept Videos

Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
1.2K
Temperature Dependent Deformation01:12

Temperature Dependent Deformation

In a nonhomogeneous rod made up of steel and brass, restrained at both ends and subjected to a temperature change, several steps are involved in calculating the stress and compressive load. Due to the problem's static indeterminacy, one end support is disconnected, allowing the rod to experience the temperature change freely. Next, an unknown force is applied at the free end, triggering deformations in the rod's steel and brass portions. These deformations are then calculated and added...
457