Impact of B₄C co-sputtering on structure and optical performance of Cr/Sc multilayer X-ray mirrors

The influence of B₄C incorporation during magnetron sputter deposition of Cr/Sc multilayers intended for soft X-ray reflective optics is investigated. Chemical analysis suggests formation of metal: boride and carbide bonds which stabilize an amorphous layer structure, resulting in smoother interfaces and an increased reflectivity. A near-normal incidence reflectivity of 11.7%, corresponding to a 67% increase, is achieved at λ = 3.11 nm upon adding 23 at.% (B + C). The advantage is significant for the multilayer periods larger than 1.8 nm, where amorphization results in smaller interface widths, for example, giving 36% reflectance and 99.89% degree of polarization near Brewster angle for a multilayer polarizer. The modulated ion-energy-assistance during the growth is considered vital to avoid intermixing during the interface formation even when B + C are added.