Effect of Solvents, Their Mixture and Thermal Annealing on the Performance of Solution Processed Polymer...

In this study, we first investigated changes seen in electrical and optical properties of a polymer light-emitting diode due to using different kinds of solvents and their mixture. Two-layer light emitting diodes with organic small molecules doped in a PVK polymer host were fabricated using (i) non-aromatic solvent chloroform with a high evaporation rate; (ii) aromatic solvent chlorobenzene with a low evaporation rate, and (iii) their mixture with different relative ratios. The effect of nano-scale layer thickness, surface roughness and internal nano-morphology on threshold voltage and the amount of electric current, the luminance and efficiency of a device were assessed. Results indicated the importance of majority charge carriers' type in the selection of solvent and tuning its properties. Then, the effect of thermal annealing on electrical and optical properties of polymer light emitting diodes was investigated. During the device fabrication, pre-annealing in 80 and/or 120 °C and post-annealing in 120 °C were performed. The nano-scale effect of annealing on polymer-metal interface and electric current injection was described thoroughly. A comparison between threshold voltage, luminance and electric current efficiency of luminescence for different annealing processes was undertaken, so that the best electric current efficiency of luminescence achieved at 120 °C pre-annealing accompanied with 120 °C post-annealing.