Enhancing surface properties of breast implants by using electrospun silk fibroin

In the present study, a new electrospun silk fibroin coating of silicone breast implants with improved biocompatibility and mechanical properties was obtained. Fibrous scaffolds were produced by electrospinning a solution containing silk fibroin, derived from Bombyx mori cocoons, and polyethylene oxide (PEO) to be used as a coating of breast implants. A randomly oriented structure of fibroin/PEO was electrospun on implants as assessed by SEM analysis, roughness measurements and ATR-FTIR spectroscopy. The scaffold showed 0.25 µm diameter fibres, 0.76 µm size superficial pores, arithmetic roughness of 0.632 ± 0.12 µm and texture aspect ratio of 0.893 ± 0.04. ATR-FTIR spectroscopy demonstrates the presence of PEO and fibroin in the coating. The mechanical characterisation of the implants before and after being coated with fibroin/PEO demonstrated that the fibroin/PEO scaffold contributes to the increase in the elastic modulus from 0.392 ± 0.02 to 0.560 ± 0.03 MPa and to a more elastic behaviour of the breast implants. Using the fibroin/PEO coating, human fibroblasts seeded on this matrix increased viability up to 30% compared to conventional breast implants. Electrospun silk fibroin could represent a clinically compatible, viable form to coat breast implants. Low cytotoxicity by the fibroin coating and its physico-chemical and mechanical properties may find application in improving breast implants biocompatibility. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1655-1661, 2018.