Optimizing Optical Absorption, Exciton Dissociation, and Charge Transfer of a Polymeric Carbon Nitride with Ultrahigh...

Polymeric or organic semiconductors are promising candidates for photocatalysis but mostly only show moderate activity owing to strongly bound excitons and insufficient optical absorption. Herein, we report a facile bottom-up strategy to improve the activity of a carbon nitride to a level in which a majority of photons are really used to drive photoredox chemistry. Co-condensation of urea and oxamide followed by post-calcination in molten salt is shown to result in highly crystalline species with a maximum π-π layer stacking distance of heptazine units of 0.292 nm, which improves lateral charge transport and interlayer exciton dissociation. The addition of oxamide decreases the optical band gap from 2.74 to 2.56 eV, which enables efficient photochemistry also with green light. The apparent quantum yield (AQY) for H₂ evolution of optimal samples reaches 57 % and 10 % at 420 nm and 525 nm, respectively, which is significantly higher than in most previous experiments.