pH-Driven Wetting Switchability of Electrodeposited Superhydrophobic Copolymers of Pyrene Bearing Acid Functions and...

A smart stimuli-responsive surface was fabricated by the electro-copolymerization of pyrene monomers followed by base and acid treatment. Copolymers of pyrenes bearing fluorinated chains (Py-nF₆ ) and acid functions (Py-COOH) were produced with different molar concentrations of each monomer (0, 25, 50, 75, and 100 % of Py-nF₆ vs. Py-COOH) by an electrochemical process. Two different perfluorinated pyrenes containing ester and amide groups were used to reach superhydrophobic properties. The relation of those bonds with the final properties of the surface was explored. The pH-sensitive group of Py-COOH allowed the surfaces to be reversibly switched from superhydrophobic (water contact angle>θ_w >150° and very low hysteresis) to hydrophilic (θ_w <90°). The amide and ester bonds influenced the recovery of the original wettability after both base and acid treatment. Although the fluorinated homopolymer with ester bonds was insensitive to base and acid treatment due to its superhydrophobic properties with ultralow water adhesion, the recovery of the original wettability for the copolymers was much more important with amide bonds due to the amide functional groups be more resistant to the hydrolysis reaction. This strategy offered the opportunity to access superhydrophobic films with switchable wettability by simple pH treatment. The films proved to be a good tool for use in biological applications, for example, as a bacterial-resistant film if superhydrophobic and as a bacterial-adherent film if hydrophilic.