Crystalline phases involved in the hydration of calcium silicate-based cements: Semi-quantitative Rietveld X-ray

Renata Grazziotin-Soares1, Mohammad H Nekoofar2,3, Thomas Davies4

  • 1College of Dentistry, University of Saskatchewan, Saskatoon, SK, Canada.

Australian Endodontic Journal : the Journal of the Australian Society of Endodontology Inc
|September 1, 2017
PubMed

Keywords:
X-ray diffraction analysischemical propertiesmineral trioxide aggregate

More Related Videos

X-ray Powder Diffraction in Conservation Science: Towards Routine Crystal Structure Determination of Corrosion Products on Heritage Art Objects09:16

X-ray Powder Diffraction in Conservation Science: Towards Routine Crystal Structure Determination of Corrosion Products on Heritage Art Objects

Published on: June 8, 2016

16.8K
Fabrication and Optimization of Type II Silicon Clathrate Films06:53

Fabrication and Optimization of Type II Silicon Clathrate Films

Published on: October 14, 2025

1.2K

Related Concept Videos

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
1.0K
Strength and Heat of Hydration01:29

Strength and Heat of Hydration

The hydration of cement is an exothermic reaction in which heat is generated as cement hydrates. This heat of hydration is critical to cement's strength development. The rate at which this heat is generated affects the temperature rise, with a majority of the heat being released early in the hydration process, half within the first three days, and about 75% within the first week.
The heat of hydration for each cement compound is significant; for instance, tricalcium aluminate (C3A) and...
766
Transition Zone01:28

Transition Zone

The transition zone in concrete is a critical area where aggregate meets cement paste, marked by a distinct porosity and weakness compared to the surrounding material. The adhesion around the aggregates is primarily due to Van Der Waals forces. The voids within this zone influence its robustness; initially, it is less durable than the surrounding bulk mortar due to larger voids. Initially, when concrete is compacted, a higher water-cement ratio near the aggregates leads to the formation of...
430
Ionic Crystal Structures02:42

Ionic Crystal Structures

Ionic crystals consist of two or more different kinds of ions that usually have different sizes. The packing of these ions into a crystal structure is more complex than the packing of metal atoms that are the same size.
Most monatomic ions behave as charged spheres, and their attraction for ions of opposite charge is the same in every direction. Consequently, stable structures for ionic compounds result (1) when ions of one charge are surrounded by as many ions as possible of the opposite...
18.6K
Drying Shrinkage01:21

Drying Shrinkage

When hardened concrete is exposed to air with a relative humidity of less than 100 percent, it begins to lose the free water within its capillaries. As this water evaporates, the water initially adsorbed onto the calcium silicate hydrates migrates towards these now empty spaces and eventually evaporates as well. Over time, as more water leaves, the volume of the concrete decreases, a phenomenon known as drying shrinkage.
A portion of this drying shrinkage can be reversed; if the concrete is...
408
Ionic Compounds: Formulas and Nomenclature03:34

Ionic Compounds: Formulas and Nomenclature

An element composed of atoms that readily lose electrons (a metal) can react with an element composed of atoms that readily gain electrons (a nonmetal) to produce ions through complete electron transfer. The compound formed by this transfer is stabilized by the electrostatic attractions (ionic bonds) between the oppositely charged ions.
88.6K