Properties of BioRoot RCS, a tricalcium silicate endodontic sealer modified with povidone and polycarboxylate

F Siboni1, P Taddei2, F Zamparini1,3

  • 1Laboratory of Biomaterials and Oral Pathology, Department of Biomedical and NeuroMotor Sciences, University of Bologna, Bologna, Italy.

International Endodontic Journal
|September 8, 2017
PubMed
Abstract

Keywords:
BioRoot RCSMTA Fillapexcalcium phosphate (apatite) nucleationcalcium releaseendodontic sealertricalcium silicate

More Related Videos

Biological Compatibility Profile on Biomaterials for Bone Regeneration10:28

Biological Compatibility Profile on Biomaterials for Bone Regeneration

Published on: November 16, 2018

13.4K
Development of Amelogenin-chitosan Hydrogel for In Vitro Enamel Regrowth with a Dense Interface08:26

Development of Amelogenin-chitosan Hydrogel for In Vitro Enamel Regrowth with a Dense Interface

Published on: July 10, 2014

15.6K

Related Concept Videos

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
1.0K
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
498
Waterproofing and Anti-Bacterial Admixtures in Concrete01:22

Waterproofing and Anti-Bacterial Admixtures in Concrete

Concrete's susceptibility to water absorption is due to the capillary action within the pores of its hydrated cement paste. This action draws water in, creating the need for waterproofing admixtures to prevent such penetration. The efficacy of these admixtures is contingent upon the water pressure, with variations arising from different conditions such as rain, capillary rise, or hydrostatic pressure in structures intended to hold water.
Waterproofing admixtures render concrete hydrophobic,...
263