Janus and Strawberry-like Particles from Azo Molecular Glass and Polydimethylsiloxane Oligomer
Chungen Hsu1, Yi Du1, Xiaogong Wang1
1Department of Chemical Engineering, Laboratory of Advanced Materials (MOE), Tsinghua University , Beijing, P. R. China 100084.
Abstract:
This study investigated Janus and strawberry-like particles composed of azo molecular glass and polydimethylsiloxane (PDMS) oligomer, focusing on controllable fabrication and formation mechanism of these unique structures and morphologies. Two materials, the azo molecular glass (IA-Chol) and PDMS oligomer (H2pdca-PDMS), were prepared for this purpose. The Janus and strawberry-like particles were obtained from the droplets of a dichloromethane (DCM) solution containing both IA-Chol and H2pdca-PDMS, dispersed in water and stabilized by poly(vinyl alcohol). Results show that the structured particles are formed through segregation between the two components induced by gradual evaporation of DCM from the droplets, which is controlled by adding ethylene glycol (EG) into the above dispersion. Without the addition of EG, Janus particles are formed through the full segregation of the two components in the droplets. On the other hand, with the existence of EG in the dispersion, strawberry-like particles instead of Janus particles are formed in the phase separation process. The diffusion of EG molecules from the dispersion medium into the droplets causes the PDMS phase deswelling in the interfacial area due to the poor solvent effect. Caused by the surface coagulation, the coalescence of the isolated IA-Chol domains is jammed in the shell region, which results in the formation of the strawberry-like particles. For the particles separated from the dispersion and dried, the PDMS oligomer phase of the Janus particles can adhere and spread on the substrate to form unique "particle-on-pad" morphology due to its low surface energy and swelling ability, while the strawberry-like particles exist as "standstill" objects on the substrates. Upon irradiation with a linearly polarized laser beam at 488 nm, the azo molecular glass parts in the particles are significantly deformed along the light polarization direction, which show unique and distinct morphologies for these two types of the particles.