A Highly Crystalline Wide-Band-Gap Conjugated Polymer toward High-Performance As-Cast Nonfullerene Polymer Solar
Haiying Jiang1, Zhen Wang1, Lianjie Zhang1
1Institute of Polymer Optoelectronic Materials & Devices, State Key Laboratory of Luminescent Materials & Devices, South China University of Technology , Guangzhou 510640, P. R. China.
Abstract:
A new wide-band-gap conjugated polymer PBODT was successfully synthesized that showed high crystallinity and was utilized as the active material in nonfullerene bulk-heterojunction polymer solar cells (PSCs). The photovoltaic devices based on the as-cast blend films of PBODT with ITIC and IDIC acceptors showed notable power conversion efficiencies (PCEs) of 7.06% and 9.09%, with high open-circuit voltages of 1.00 and 0.93 V that correspond to low energy losses of 0.59 and 0.69 eV, respectively. In the case of PBODT:ITIC, lower exciton quenching efficiency and monomolecular recombination are found for devices with small driving force. On the other hand, the relatively higher driving force and suppressed monomolecular recombination for PBODT:IDIC devices are identified to be the reason for their higher short-circuit current density (Jsc) and higher PCEs. In addition, when processed with the nonchlorinated solvent 1,2,4-trimethylbenzene, a good PCE of 8.19% was still achieved for the IDIC-based device. Our work shows that such wide-band-gap polymers have great potential for the environmentally friendly fabrication of highly efficient PSCs.