UDM enhanced physical and mechanical properties through the formation of nanocavities in an epoxy matrix

Kaushal Kumar1, Arun Kumar1, P K Ghosh1

  • 1Department of Metallurgical & Materials Engineering, Indian Institute of Technology Roorkee, Roorkee 247667, India.

Ultrasonics Sonochemistry
|September 27, 2017
PubMed

Keywords:
Epoxy based polymersMechanical propertiesNanocavitiesThermal analysisUltrasonic dual mixing

More Related Videos

Application of a Coupling Agent to Improve the Dielectric Properties of Polymer-Based Nanocomposites06:34

Application of a Coupling Agent to Improve the Dielectric Properties of Polymer-Based Nanocomposites

Published on: September 19, 2020

6.4K
Nanosponge Tunability in Size and Crosslinking Density11:15

Nanosponge Tunability in Size and Crosslinking Density

Published on: August 4, 2017

8.1K

Related Concept Videos

Accelerated Curing of Concrete01:25

Accelerated Curing of Concrete

Accelerating concrete curing is achieved by applying heat and additional moisture. This process accelerates the hydration of the cement, resulting in an earlier strength gain in the concrete. Steam curing is a method wherein the concrete products are either transported through a chamber on a conveyor belt or encased in plastic, allowing steam at atmospheric pressure to circulate freely around them. This process begins with a phase of moist curing that typically lasts between 3 to 5 hours, after...
507
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...
510
Fiber Reinforced Concrete01:22

Fiber Reinforced Concrete

Fiber-reinforced concrete significantly enhances the structural and nonstructural properties of traditional concrete by incorporating fibers like steel, glass, and polymers. These fibers, varying from natural ones such as sisal and cellulose to manufactured ones like polypropylene and Kevlar, are mixed into hydraulic cement with aggregates. Steel fibers, often preferred for their robustness, contribute to improved ductility, toughness, and post-cracking performance. The concrete is classified...
444
Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
494