Structural Regulation and Electroconductivity Change of Nitrogen-Doping Reduced Graphene Oxide Prepared Using
Tiefeng Peng1, Hongjuan Sun2,3, Tongjiang Peng4,5
1Key Laboratory of Ministry of Education for Solid Waste Treatment and Resource Recycle, Southwest University of Science and Technology, Mianyang 621010, China. pengtiefeng@cqu.edu.cn.
Abstract:
Using p-phenylene diamine (PPD) as a modifier and nitrogen resource, nitrogen-doping reduced graphene oxide was prepared by one-step refluxing method. The influence of PPD-GO (graphene oxide) mass ratio X on surface functional groups, layer structure, and electroconductivity of nitrogen-doping reduced grapheme oxide (NRGO-X) was investigated by Fourier Transform Infrared Spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), UV-vis absorption spectrum, and electrical measurement. The results showed that GO can be simultaneously reduced and nitrogen-doped by PPD. When PPD-GO mass ratio X ≤ 6, there existed three types of N configurations in NRGO-X, including pyridinic N, pyrrolic N, and graphitic N. However, when X > 6, the pyridinic N disappeared in a six-membered ring. Further, the reduction process of NRGO as well as the nitrogen doping level and type can be regulated by changing the mass ratio X. With the increase of X, the d-spacing of NRGO-X layers increased first and then decreased, while the electrical conductivity increased gradually.