Heteroepitaxial diamond growth on 4H-SiC using microwave plasma chemical vapor deposition

Deposition of heteroepitaxial diamond via microwave chemical vapor deposition has been performed on a 4H-SiC substrate using bias enhanced nucleation followed by a growth step. In future work, the diamond film will serve as a protective layer for an alpha particle sensor designed to function in an electrorefiner during pyroprocessing of spent fuel. The diamond deposition on the 4H-SiC substrate was carried out using a methane-hydrogen gas mixture with varying gas flow rates. The nucleation step was conducted for 30 minutes and provided sufficient nucleation sites to grow a diamond film on various locations on the substrate. The resulting diamond film was characterized using Raman spectroscopy exhibiting the strong Raman peak at 1332 cm^-1. Scanning electron microscopy was used to observe the surface morphology and the average grain size of the diamond film was observed to be on the order of ∼2-3 μm.