Sustained raloxifene release from hyaluronan-alendronate-functionalized titanium nanotube arrays capable of enhancing...

To enhance the localized bone remodeling at titanium-based implants under osteoporotic conditions, TiO₂ nanotube arrays (TNT) were used as nanoreserviors for raloxifene (Ral) and then covered with the hybrid multilayered coating of chitosan and alendronate grafted hyaluronic acid (HA-Aln) via a spin-assisted layer-by-layer technique. The fabrication of this system (TNT/Ral/LBL-Aln) was characterized by field emission scanning electron microscopy (SEM), atomic force microscope (AFM) and X-ray photoelectron spectroscopy (XPS), respectively. The release test showed that the composited multilayers onto Ral-loaded TiO₂ nanotube substrate (TNT/Ral) could prevent the burst release of Ral from TiO₂ nanotube arrays and maintain stable Ral concentration at the implant site even after 192h. The TNT/Ral/LBL-Aln system demonstrated higher alkaline phosphatase (ALP) activity, mineralization capability in osteoblasts as well as lower tartrate-resistant acid phosphatase (TRAP) activity in osteoclasts compared to both bare TiO₂ nanotube and TNT/Ral substrate, respectively. Moreover, the in vivo tests of micro-CT, histological staining and push-out testing showed that TNT/Ral/LBL-Aln implant could efficiently enhance the formation of new bone around the implant and promote bone binding in osteoporotic rabbits. The study indicated the potential application of TNT/Ral/LBL-Aln system for bone remodeling under osteoporotic condition.