Effect of thickness and surface modifications on flexural strength of monolithic zirconia

Fusun Ozer1, Andrew Naden2, Volkan Turp3

  • 1Associate Professor, University of Pennsylvania School of Dental Medicine, Department of Preventive and Restorative Sciences, Philadelphia, Pa.

The Journal of Prosthetic Dentistry
|October 19, 2017
PubMed
Abstract

Keywords:
monolithic zirconiaflexural strengthdental restorationssurface modificationin vitro study

More Related Videos

Fused Filament Fabrication FFF of Metal-Ceramic Components08:43

Fused Filament Fabrication FFF of Metal-Ceramic Components

Published on: January 11, 2019

18.2K
Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

894

Related Concept Videos

Flexural Stress01:16

Flexural Stress

When analyzing bending in symmetric members, it's crucial to understand how stresses distribute when subjected to bending moments. This stress distribution is effectively described by applying fundamental mechanics and material science principles, particularly Hooke's Law for elastic materials.
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
788
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
623
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen...
610
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
604
Impact Strength of Concrete01:21

Impact Strength of Concrete

Impact strength in concrete is a critical measure that reflects the material's capability to endure the forces applied during pile driving and when supporting machinery foundations that experience impulsive loads. It is also essential when handling precast concrete components to prevent accidental damage. The impact strength is assessed by observing the concrete's resistance to repeated impacts and energy absorption capacity. A key indicator of significant damage to concrete is when it...
640
Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity01:15

Relation between Poisson's ratio, Modulus of Elasticity and Modulus of Rigidity

Deformation occurs in axial and transverse directions when an axial load is applied to a slender bar. This deformation impacts the cubic element within the bar, transforming it into either a rectangular parallelepiped or a rhombus, contingent on its orientation. This transformation process induces shearing strain. Axial loading elicits both shearing and normal strains. Applying an axial load instigates equal normal and shearing stresses on elements oriented at a 45° angle to the load axis.
635