Pd supported on carbon containing nickel, nitrogen and sulfur for ethanol electrooxidation

Carbon material containing nickel, nitrogen and sulfur (Ni-NSC) has been synthesized using metal-organic frameworks (MOFs) as precursor by annealing treatment with a size from 200 to 300 nm. Pd nanoparticles supported on the Ni-NSC (Pd/Ni-NSC) are used as electrocatalysts for ethanol oxidation in alkaline media. Due to the synergistic effect between Pd and Ni, S, N, free OH radicals can form on the surface of Ni, N and S atoms at lower potentials, which react with CH₃CO intermediate species on the Pd surface to produce CH₃COO^- and release the active sites. On the other hand, the stronger binding force between Pd and co-doped N and S is responsible for enhancing dispersion and preventing agglomeration of the Pd nanoparticles. The Pd(20 wt%)/Ni-NSC shows better electrochemical performance of ethanol oxidation than the traditional commercial Pd(20 wt%)/C catalyst. Onset potential on the Pd(20 wt%)/Ni-NSC electrode is 36 mV more negative compared with that on the commercial Pd(20 wt%)/C electrode. The Pd(20 wt%)/Ni-NSC in this paper demonstrates to have excellent electrocatalytic properties and is considered as a promising catalyst in alkaline direct ethanol fuel cells.