A robotic magnetic nanoparticle solid phase extraction system coupled to flow-batch analyzer and GFAAS for...

A lab-made magnetic-mechanical robotic (MMR) system coupled to a flow-batch analyzer (FBA) for magnetic nanoparticles solid phase extraction (MSPE) is presented. As an illustrative application, an NMR-FBA couple was connected to a graphite furnace atomic absorption spectrometer (GFAAS) for quantification of trace cadmium in edible oils. Factors affecting MSPE, such as the amount of adsorbent, the type, concentration and volume of the eluent and elution time were studied. Under the optimized experimental conditions, the interferents studied did not reveal a significant change in the analytical response, indicating that proposed method is selective. The sampling rate, characteristic mass, working linear range, limits of detection (LOD), and sensitivity were 10h^-1, 0.18pg, 0.05-1.0μgkg^-1, 0.006μgL^-1, and 0.4197, respectively. An enrichment factor of 9 was achieved using a 2.5mL oil sample. In order to evaluate the accuracy, a certified reference material was analyzed by the proposed and a reference method. The values obtained were compared with the one provided from the manufacturer and no statistically significant differences were observed among three values at a confidence level of 95% using paired t-test. In addition, the precision intra-day and inter day of the proposed method and the robustness were assessed and again no statistically significant differences were observed at a confidence level of 95%. The use of a microcolumn to immobilize the MNPs is not needed with the proposed MMR-FBA-GFAAS system, thus avoiding the well-known problem of non-uniform packing of the MNPs presented in previous flow-based automatic methods. Despite a high organic load of edible oils, the method developed is simple, robust and presents satisfactory analytical features when compared with others that have been reported in the literature, suggesting that it is a potentially useful alternative to determine trace analytes in viscous matrices without external pretreatment.