Preparation of Solution Blown Polyamic Acid Nanofibers and Their Imidization into Polyimide Nanofiber Mats

Solution blow spinning (SBS) is an innovative process for spinning micro/nanofibers. In this paper, polyamic acid (PAA) nanofibers were fabricated via a SBS apparatus and then imidized into polyimide (PI) nanofibers via thermal process. The morphology and diameter distributions of PAA nanofibers were determined by scanning electron microscope (SEM) and Image Tool software, the processing parameters, including PAA concentration, solution feeding rate, gas pressure, nozzle size, and receiving distance were investigated in details. The fourier transform infrared spectroscopy (FTIR) was used to characterize the chemical changes in the nanofibers after thermal imidization. The results showed that the solution concentration exhibited a notable correlation with spinnability, and the formation of bead defects in PAA nanofibers. Solution feeding rate, gas pressure, nozzle size, and receiving distance affected nanofiber production efficiency and diameter distribution. The average diameters of fibers produced ranged from 129.6 to 197.7 nm by varying SBS parameters. Precisely, PAA nanofibers with good morphology were obtained and the average diameter of nanofibers was 178.2 nm with optimum process parameter. After thermal imidization, the PI nanofibers exhibited obvious adhesion morphology among interconnected fibers, with an increased average diameter of 209.1 nm. The tensile strength of resultant PI nanofiber mat was 12.95 MPa.