Preparation of Lithium Titanate/Reduced Graphene Oxide Composites with Three-Dimensional "Fishnet-Like" Conductive...

With use of ammonium chloride (NH₄Cl) as the pore-forming agent, three-dimensional (3D) "fishnet-like" lithium titanate/reduced graphene oxide (LTO/G) composites with hierarchical porous structure are prepared via a gas-foaming method. Scanning electron microscopy and transmission electron microscopy images show that, in the composite prepared with the NH₄Cl concentration of 1 mg mL^-1 (1-LTO/G), LTO particles with sizes of 50-100 nm disperse homogeneously on the 3D "fishnet-like" graphene. The nitrogen-sorption analyses reveal the existence of micro-/mesopores, which is attributed to the introduction of NH₄Cl into the gap between the graphene sheets that further decomposes into gases and produces hierarchical pores during the thermal treatment process. The loose and porous structure of 1-LTO/G composites enables the better penetration of electrolytes, providing more rapid diffusion channels for lithium ion. As a result, the 1-LTO/G electrode delivers an ultrahigh specific capacity of 176.6 mA h g^-1 at a rate of 1 C. Even at 3 and 10 C, the specific capacity can reach 167.5 and 142.9 mA h g^-1, respectively. Moreover, the 1-LTO/G electrode shows excellent cycle performance with 95.4% capacity retention at 10 C after 100 cycles. The results demonstrate that the LTO/G composite with these properties is one of the most promising anode materials for lithium-ion batteries.