Modification of chitosan/calcium alginate/Fe₃O₄ hydrogel microsphere for enhancement of Cu(II) adsorption

Copper in drinking water causes a significant environmental problem. Composite material based on alginate hydrogel has been gaining attention in the field of Cu(II) adsorption. However, alginate-based hydrogel exhibits poor mechanical property and relative low adsorption capacity which limit their application. The present study is devoted to the modification of chitosan/calcium alginate/Fe₃O₄ (CAF) hydrogel microsphere by NaOH solution for enhancement of Cu(II) adsorption. Results reveal that modification of CAF via NaOH solution significantly improves the mechanical strength and Cu²⁺ adsorption capacity of pristine materials. FTIR and XRD analysis confirms that CAF and newly prepared materials (NACAF) are successfully prepared. SEM and EDX are employed to analyze the surface morphology and elemental composition, respectively, both before and after their loading with Cu²⁺. XPS study demonstrates adsorption mechanism is based on chelation and ion-exchange. Compressive stress-strain curves demonstrate NACAF has better mechanical performance than CAF. The adsorption kinetics of the two adsorbents follow a pseudo-second-order model. The equilibrium data were best described by Langmuir isotherm model, and the estimated maximum equilibrium sorption capacity, q _m,is 261.31 mg/g for the NACAF, which is larger than that of CAF (145.39 mg/g). Hence, NACAF shows excellent mechanical strength and high sorption capacity for Cu²⁺. It has great potential for Cu(II) removal in aqueous solutions.