From Positive to Negative Zero-Field Splitting in a Series of Strongly Magnetically Anisotropic Mononuclear Metal...

A series of mononuclear [M(hfa)₂(pic)₂] (Hhfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedione; pic = 4-methylpyridine; M = Fe^II, Co^II, Ni^II, Zn^II) compounds were obtained and characterized. The structures of the complexes have been resolved by single-crystal X-ray diffraction, indicating that, apart from the zinc derivative, the complexes are in a trans configuration. Moreover, a dramatic lenghthening of the Fe-N distances was observed, whereas the nickel(II) complex is almost perfectly octahedral. The magnetic anisotropy of these complexes was thoroughly studied by direct-current (dc) magnetic measurements, high-field electron paramagnetic resonance, and infrared (IR) magnetospectroscopy: the iron(II) derivative exhibits an out-of-plane anisotropy (D_Fe = -7.28 cm^-1) with a high rhombicity, whereas the cobalt(II) and nickel(II) complexes show in-plane anisotropy (D_Co ∼ 92-95 cm^-1; D_Ni = 4.920 cm^-1). Ab initio calculations were performed to rationalize the evolution of the structure and identify the excited states governing the magnetic anisotropy along the series. For the iron(II) complex, an out-of-phase alternating-current (ac) magnetic susceptibility signal was observed using a 0.1 T dc field. For the cobalt(II) derivative, the ac magnetic susceptibility shows the presence of two field-dependent relaxation phenomena: at low field (500 Oe), the relaxation process is beyond single-ion behavior, whereas at high field (2000 Oe), the relaxation of magnetization implies several mechanisms including an Orbach process with U_eff = 25 K and quantum tunneling of magnetization. The observation by μ-SQUID magnetization measurements of hysteresis loops of up to 1 K confirmed the single-ion-magnet behavior of the cobalt(II) derivative.