Melamine-containing polyphosphazene wrapped ammonium polyphosphate: A novel multifunctional organic-inorganic hybrid
Shuilai Qiu1, Chao Ma2, Xin Wang2
1State Key Laboratory of Fire Science, University of Science and Technology of China,96 Jinzhai Road, Hefei, Anhui, 230026, PR China; Department of Architecture and Civil Engineering, City University of Hong Kong, Tat Chee Avenue, Kowloon, Hong Kong.
Abstract:
To achieve superior fire safety epoxy resins (EP), a novel multifunctional organic-inorganic hybrid, melamine-containing polyphosphazene wrapped ammonium polyphosphate (PZMA@APP) with rich amino groups was prepared and used as an efficient flame retardant. Thanks to the cross-linked polyphosphazene part, PZMA@APP exhibited high flame retardant efficiency and smoke suppression to the EP composites. Thermogravimetric analysis indicated that PZMA@APP significantly enhanced the thermal stability of EP composites. The obtained sample passed UL-94 V-0 rating with 10.0wt% addition of PZMA@APP. Notably, inclusion of incorporating PZMA@APP leads to significantly decrease on fire hazards of EP, for instance, bring about a 75.6% maximum decrease in peak heat release rate and 65.9% maximum reduction in total heat release, accompanied with lower smoke production rate and higher graphitized char layer. With regards to mechanical property, the glass transition temperature of EP/PZMA@APP10.0 was as high as 184.5°C. In particular, the addition of PZMA@APP did not worsen the mechanical properties, compared to pure APP. It was confirmed that the participation of melamine-containing polyphosphazene could significantly enhance the quality of char layer and thereby resulting the higher flame retardant efficiency of PZMA@APP.