Bead debonding from a modern cementless total hip femoral component with concomitant taper corrosion

Adam I Edelstein1, Duy L Phan2, Scott M Sporer2,3

  • 1Department of Orthopaedic Surgery, Northwestern University, Feinberg School of Medicine, Chicago, IL, USA.

Arthroplasty Today
|December 6, 2017
PubMed

Keywords:
Bead sheddingTaper corrosionTotal hip arthroplasty

More Related Videos

Biotribological Testing and Analysis of Articular Cartilage Sliding against Metal for Implants09:08

Biotribological Testing and Analysis of Articular Cartilage Sliding against Metal for Implants

Published on: May 14, 2020

4.3K
Imaging of the Microstructural Failure Mechanism in the Human Hip08:43

Imaging of the Microstructural Failure Mechanism in the Human Hip

Published on: September 29, 2023

1.4K

Related Concept Videos

Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
600
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
998
Mortar Joint Deterioration in Masonry01:13

Mortar Joint Deterioration in Masonry

Mortar joint deterioration is a significant concern in masonry structures, with water accumulation in the joints leading to damage from freeze-thaw cycles. The repeated expansion of water during freezing and its melting during thawing develop and propagate cracks in the masonry joints. Eventually, this leads to the spalling of mortar from the joints, loosening masonry units and weakening the structure. The deteriorated mortar joints are also vulnerable to moisture intrusion into the walls.
The...
362