Low Pressure Vapor-assisted Solution Process for Tunable Band Gap Pinhole-free Methylammonium Lead Halide Perovskite Films
Published on: September 8, 2017
Improved Efficiency and Stability of Perovskite Solar Cells Induced by CO Functionalized Hydrophobic Ammonium-Based
Zhifang Wu1, Sonia R Raga1, Emilio J Juarez-Perez1
1Energy Materials and Surface Sciences Unit (EMSS), Okinawa Institute of Science and Technology Graduate University (OIST), 1919-1 Tancha, Onna-son, Kunigami-gun, Okinawa, 904-0495, Japan.
Abstract:
Because of the rapid rise of the efficiency, perovskite solar cells are currently considered as the most promising next-generation photovoltaic technology. Much effort has been made to improve the efficiency and stability of perovskite solar cells. Here, it is demonstrated that the addition of a novel organic cation of 2-(6-bromo-1,3-dioxo-1H-benzo[de]isoquinolin-2(3H)-yl)ethan-1-ammonium iodide (2-NAM), which has strong Lewis acid and base interaction (between CO and Pb) with perovskite, can effectively increase crystalline grain size and reduce charge carrier recombination of the double cation FA0.83 MA0.17 PbI2.51 Br0.49 perovskite film, thus boosting the efficiency from 17.1 ± 0.8% to 18.6 ± 0.9% for the 0.1 cm2 cell and from 15.5 ± 0.5% to 16.5 ± 0.6% for the 1.0 cm2 cell. The champion cell shows efficiencies of 20.0% and 17.6% with active areas of 0.1 and 1.0 cm2 , respectively. Moreover, the hysteresis behavior is suppressed and the stability is improved. The result provides a promising route to further elevate efficiency and stability of perovskite solar cells by the fine tuning of triple organic cations.